Just saw the thread.

Coffee etch is the latest rage in knifemaking. Before that it was "baked on brown or black lacquer".
I find ferric to be as good as one gets on wootz and some old wootz etches better than others. Some prefer nitric. Both used in very dilute forms.
Some come away very black with ferric and others whiteish. I assume it is slight internal chemistries which cause the coloration variables. Heat treatment does play a part as well and the cause of most etching coloration issues within a single bar as with the blades shown above in the thread.

I have not found the carbides to go away till high into the bright orange colors when forging and even then you can bring them back if you further play with heat. As we have all seen the weld joints on Indian blades show a black weld line and white on either side and then pattern as we expect. I promise you that those have reached a full welding temp when they are made....or repaired...the jury is still out on why they have those welds...the record I have seen was a Tulwar in Jodhpur, India with three welds...meaning four pieces.

I will shortly begin a project which will have several wootz welds. No need to post it here as it is modern material all around.

Ric
Richard Furrer is offline   Reply With Quote
Old 13th February 2020, 04:56 AM   #32
ALEX
Member
 
ALEX's Avatar
 
Join Date: Jan 2006
Posts: 917
Default

Quote:
Originally Posted by Drabant1701
... Now this may be a silly question, but I have to ask. Do you think its possible to make a Nital like etching solution for wootz using the gold testing solutions?...


I'd not recommend experimenting with it. It could work or it could damage the blade. Good wootz will react to most mild etchants like lemon juice or any household cleaning solution containing acid (like muriatic acid), I heard even Coca-Cola and coffee do the job although never tried them as I use FeCl and also generic household cleaner containing muriatic acid... whatever darkens the steel without potential to damage it.
ALEX is offline   Reply With Quote
Reply


Thread Tools Search this Thread
Search this Thread:

Advanced Search
Display Modes

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

vB code is On
Smilies are On
[IMG] code is On
HTML code is Off
Forum Jump



All times are GMT. The time now is 02:07 PM.


Powered by: vBulletin Version 3.0.3
Copyright ©2000 - 2020, Jelsoft Enterprises Ltd.
Posts are regarded as being copyrighted by their authors and the act of posting material is deemed to be a granting of an irrevocable nonexclusive license for display here.