Richard Furrer · 1st October 2008, 02:10 PM

Hello All,
This may not be exactly what is discussed here, but it does involve a rivet on a blade...

I have seen rivets holding on a portion of wootz near the spine which had broken off due to the seam on the spine causing a weakness (the seam or dark line on the spine of some wootz blades being the top of the ingot which can fold over during forging or may contain poor metals from the melt)...the rivet was also wootz...

Also do not discount the idea that a contrasting metal, filework, fullers or even a carving (horimono on Japanese blades) were used to hide a flaw in the steel...a poor weld or inclusion or a crack from hardening etc.

Ric

1st October 2008, 02:10 PM	#10
Richard Furrer Member Join Date: Mar 2006 Location: Sturgeon Bay, Wisconsin Posts: 163	Hello All, This may not be exactly what is discussed here, but it does involve a rivet on a blade... I have seen rivets holding on a portion of wootz near the spine which had broken off due to the seam on the spine causing a weakness (the seam or dark line on the spine of some wootz blades being the top of the ingot which can fold over during forging or may contain poor metals from the melt)...the rivet was also wootz... Also do not discount the idea that a contrasting metal, filework, fullers or even a carving (horimono on Japanese blades) were used to hide a flaw in the steel...a poor weld or inclusion or a crack from hardening etc. Ric