blue lander · 7th April 2015, 09:24 PM

I'll give it a nice light scrubbing and polish... The pitting looks too deep to do anything about. Is the hot vinegar treatment the best way to get an etch out of this?

Rick · 7th April 2015, 09:39 PM

I believe the furniture is silver; this was probably once a very nice sword .
Then again any of these old soldiers that have survived have intrinsic worth .

http://en.wikipedia.org/wiki/Moro_Re...2.80.931913.29

blue lander · 7th April 2015, 09:56 PM

I got that impression too, this used to be a smart little weapon. It seems like a lot of fine detail has been worn off this thing over the ages.

And maybe its just me but the bandage wrapped hilt has the color of dried blood

Sajen · 7th April 2015, 09:56 PM

Quote:

Originally Posted by blue lander

I'll give it a nice light scrubbing and polish... The pitting looks too deep to do anything about. Is the hot vinegar treatment the best way to get an etch out of this?

Don't be to fast. I still see hard crusted corrosion on the blade. The deep pitting you of course don't will get polished away. Maybe try to bath the blade inside lemon acid or vinegar essence to remove all corrosion. After this is done polish the blade with fine sandpaper. When this is done you can etch the blade. For the etching do a little bit search in old threads, there are different etching solutions which can be used. Like Rick I think this kris is worth to be preserved.

Regards,
Detlef

Spunjer · 8th April 2015, 12:52 PM

nothing more i can add from what the others said other than congrats in acquiring this complete set. at first glance, it looks like scabbard is original to the blade, and most likely, as you have mentioned, the fittings on the handle are silver. can't wait to see how this piece looks like all cleaned up!

blue lander · 20th April 2015, 07:10 PM

It arrived yesterday, I haven't had a chance to take a picture yet. I cleaned it off and gave it a once over with vinegar - the core of the blade turns a much lighter color than the cheeks. I don't see any lamination patterns yet.

The dark/light steel comes up much better on one side over the other
unfortunately the good side is nearly entirely covered in corrosion.

blue lander · 24th April 2015, 02:23 AM

Got a little better results with diluted fecl...

Only so much I can do with all that corrosion thoguh

7th April 2015, 09:39 PM	#2
Rick Vikingsword Staff Join Date: Nov 2004 Posts: 6,376	I believe the furniture is silver; this was probably once a very nice sword . Then again any of these old soldiers that have survived have intrinsic worth . http://en.wikipedia.org/wiki/Moro_Re...2.80.931913.29 Last edited by Rick; 7th April 2015 at 09:56 PM.

24th April 2015, 02:23 AM	#7
blue lander Member Join Date: Nov 2013 Posts: 456	Got a little better results with diluted fecl... Only so much I can do with all that corrosion thoguh Attached Images

7th April 2015, 09:24 PM	#1
blue lander Member Join Date: Nov 2013 Posts: 456	I'll give it a nice light scrubbing and polish... The pitting looks too deep to do anything about. Is the hot vinegar treatment the best way to get an etch out of this?

7th April 2015, 09:56 PM	#3
blue lander Member Join Date: Nov 2013 Posts: 456	I got that impression too, this used to be a smart little weapon. It seems like a lot of fine detail has been worn off this thing over the ages. And maybe its just me but the bandage wrapped hilt has the color of dried blood

8th April 2015, 12:52 PM	#5
Spunjer Member Join Date: Dec 2004 Location: Witness Protection Program Posts: 1,730	nothing more i can add from what the others said other than congrats in acquiring this complete set. at first glance, it looks like scabbard is original to the blade, and most likely, as you have mentioned, the fittings on the handle are silver. can't wait to see how this piece looks like all cleaned up!

20th April 2015, 07:10 PM	#6
blue lander Member Join Date: Nov 2013 Posts: 456	It arrived yesterday, I haven't had a chance to take a picture yet. I cleaned it off and gave it a once over with vinegar - the core of the blade turns a much lighter color than the cheeks. I don't see any lamination patterns yet. The dark/light steel comes up much better on one side over the other unfortunately the good side is nearly entirely covered in corrosion.