Damascus Saber for appreciation / Sable de Damasco para apreciación

[broadaxe]

Nice presentation saber, the steel appears to be legit pattern welded in original (past) etched condition. I've several, mostly can be dated to 1860-1880 era.
Bulat is the russian word for wootz, derived from Farsi - fulad. In its turn probably derived from the Hebrew word for steel plada.

[spiral]

Originally Posted by Fernando K

If the the "scroll" pattern is an etching, the bottom should show the damascus pattern. I do not think the bottom has been polished so much that it removed the effect or pattern.

However the issue of "recazo" remains. I think if the blade were Damascus, the pattern would stand out in an important part.

I have the catalog of a signature similar to - Eichhorn - sabers for all parts of the world - including the United States and Europe, and there is no single damascus example.

Affectionately. Fernando K

Thanks Broadaxe for the confirmation re. Bulat etc.

Hello again Fernando,

Ido understand your thoughts, but it is a laminated blade, I can "see" it is, Ive etched many,many blades.

Decorative etches & stamped riccasos can be finnished off without showing the blade structure. This did used to be done in Germany.

But if you wish to belive own thoughts, then please do! our thoughts help govern our lives after all, so we are used to trusting them. { I must admit this forum has finaly after many years also taught me that its pointless {or timewaisting.} to argue facts against peoples beliefs....}

But either way enjoy it, Its an interesting sword!


Best regards,
Spiral

[Fernando K]

Hola a todos:

Humildemente, puedo tener mis propias creencias, pero demando que alguien me explique como la parte decorativa, "scroll", sometida a la accion del ácido, no muestra el patron o diseño del damascus.

Afectuosamente. Fernando K

Hi all:

Humbly, I can have my own beliefs, but request that someone explain to me how the decorative, "scroll", under the action of acid, does not show the damascus pattern or design.

Affectionately. Fernando K

[spiral]

I Am not a German cutler from 1870, but know they could do such thing.

Perhaps One can deep etch the "floral work" to give depth, then lighty polish to leave the "floral etch" but smothing out the steel laminations?

As I say Ive seen such work before, but Cutlers then were very skilled, I am just an amater hobbyist.

I to would like to know how such work was done!..... Perhaps Bernard Levine on Bladeforums would know? or one of the foromites there? several are Germans with great knowledge of there old cutlers.

Spiral

PS. I think it is against forum rules to post in other languages than English ?: Or perhaps Ive misunderstood that? It seems more common now than a few years ago perhaps the rules have changed?

[Emanuel]

Hello,

Nice to see this old German pattern welding.

Spiral, I believe Fernando explained in one of his first posts that he is using a translator to communicate. The Spanish is translated below in English and he is including the original Spanish in case the translation is faulty and to preserve his meaning

Now this patterning was done purely for aesthetic purposes, was it not? By the 1870s Germany was producing large quantities of cast steel if I recall correctly.

Cheers,
Emanuel

[spiral]

Ahh that makes sense the Emmanuel! {Re. the Spanish.}

Decorative? I expect so! More costly? Definatly!

Spiral

[Ibrahiim al Balooshi]

Salaams all~ As Spiral was saying...is this not a laminated blade? If so it must have been given the wootz treatment afterwards no? That would explain why it is not damascened on the scrolls. What then is or was the process?
Regards,
Ibrahiim al Balooshi.