Default How to heat treat wootz?



Hi guys.

Recently I bought a piece of ancient wootz steel. Yeah, It's a real and authentic one identified by an authorized organization and a senior researcher.

My friend and I would like to make two blades from it. I think the knifemaker will use grinding removing method to shape the blades.

As I knew, you guys are always willing to give people some nice advices.

Any suggestions on treatments of quenching, annealing, tempering and finish are appreciated.

Thanks a lot.
Attached Images
 
shangrila is offline   Reply With Quote
Old 4th February 2010, 07:26 PM   #2
mross
Member
 
Join Date: Jan 2005
Posts: 478
Default

I would ask this in bladeforums.com or forums.dfoggknives.com. It's tricky stuff and if you don't do it right you loose the pattern. If you can find reference material from Al Pendry that would be helpful. There are some folks at bladeforums.com that work in modern wootz.
mross is offline   Reply With Quote
Old 5th February 2010, 08:08 PM   #3
t_c
Member
 
Join Date: Jun 2006
Location: ca, usa
Posts: 92
Default

There was also an article in the Journal of Asian Martial Arts that you might find usefull as well:

Volume 17 Number 1
t_c is offline   Reply With Quote
Old 5th February 2010, 11:54 PM   #4
ariel
Member
 
ariel's Avatar
 
Join Date: Dec 2004
Location: Ann Arbor, MI
Posts: 5,503
Default

I am not a bladesmith, and know next to nothing about metallurgy. Perhaps, you are. However, having read some stuff on wootz blade making, I am awed by the complexity of the process, the degree of our current ignorance and the multitude of technicalities that can go wrong: from heating, to quenching, to just hammering, to...

Are you sure you are willing to risk this valuable material? Perhaps, just buying 2 old persian or indian blades might be cheaper in the long run.
Just an opinion...
ariel is offline   Reply With Quote
Old 7th February 2010, 02:26 PM   #5
kisak
Member
 
kisak's Avatar
 
Join Date: Jul 2008
Location: Stockholm
Posts: 182
Default

From what I can recall, wootz needs a heat cycling treatment for the pattern to fully develop. Forging could put it through this as a side effect, but for stock removal I would then guess your friend might have to do a dedicated heat cycling process. I'm not sure quite what temperature you'd aim for, but since the idea is to get carbides to shrink/grow without changing the overall structure, it would seem to me that the target temperature for each cycle would be just below A1.

For austenisation, given the high carbon content we most likely have here, I would guess that it's important not to go any higher above A1 than absolutely necessary, to keep the carbon content of the austenite in the "reasonable" region, and to preserve the pattern.
kisak is offline   Reply With Quote
Reply

Thread Tools Search this Thread
Search this Thread:

Advanced Search
Display Modes

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off

Forum Jump


All times are GMT +1. The time now is 12:43 PM.


Powered by vBulletin® Version 3.8.11
Copyright ©2000 - 2024, vBulletin Solutions Inc.
Posts are regarded as being copyrighted by their authors and the act of posting material is deemed to be a granting of an irrevocable nonexclusive license for display here.