Archaic kris for comment

[xasterix]

Originally Posted by milandro

Hello Xasterix,

thank you very much for getting back to this thread with such relevant information and very well done for returning the acquired kris to the family of the original owner. You are a gentleman.

Anyway.

Thanks for sharing your experience and your personal recipe.

I am considering all options for my one Moro blade (which I did publish elsewhere in another thread but I can add a picture here for completeness of the discussion).

I don't think it has a twist core or any other major feature , yet, I think that giving it the chance to show the hidden secrets (so to speak) may be a nice touch.

I am going to consult a local master bladesmith , hoping that he can provide some insights from a " de visu" exam of the blade.

Thanks for the kind words Milandro! I'm betting that your kris is laminated, and that the hardening at the edges will be marked neatly once it's etched (as to how dark, light, or contrasted, that'll depend on your etch media and strength). Good luck, and let us know how it goes!

[Sajen]

Hello Xas,

Be careful with your blades, I see brown corrosion by your kris, this is what Kai mentioned before about etching with FeCl.

Regards,
Detlef

[xasterix]

Originally Posted by Sajen

Hello Xas,

Be careful with your blades, I see brown corrosion by your kris, this is what Kai mentioned before about etching with FeCl.

Regards,
Detlef

Hullo Detlef! Thanks for the heads-up- but that's no corrosion don't worry- it's the "effect" of etching with white vinegar + brass residue =) it gives a different tinge to the etch which I fancy (but I understand it's not for everyone's aesthetic). Here's some more pics.