Quote:
|
Originally Posted by mariusgmioc
Cire-perdue (lost-wax) process maybe if it were bronze but almost certainly not iron.
|
I think sand casting would be the method for making an iron / steel hilt, lost wax is good for metals with a low melting point. With sand casting I do not think you would get as much detail as you would with lost wax.