Quote:
Originally Posted by A. G. Maisey
The King Tut blade is a large, serious, very well made blade, something that without prior knowledge could very well be attributed to a much later time.
I believe that it will eventually be confirmed that this blade is of forge welded construction.
|
That would be no surprise. Given that it's hot-forged*, it's not a big step to welding. Either folded and welded for homogeneity, or separate pieces welded together to get a larger piece of iron. Or both.
* The best information I've been able to find is that it isn't cold-forged (unlike the other iron objects from the tomb).