Nice Sulu kris there. Good catch!! Yup, I must agree that most Moro kris do not have good results after using arsenic (warangan) as it may turn splotchy at some areas. Very dirty look. But personnal I have seen only one piece which turn out to be very outstanding after using warangan etching.
I am also curious about the bottom stem. I think this is not common.
|