Quote:
|
Originally Posted by kai
Your blade does seem to be a genuine antique sewar. To be frank, the heavy pitting seems to be from excessive etching (and/or neglect). If it were not looking like a pretty much lost case, I would think about reworking/repolishing/staining the blade. I don't think this is feasible with this piece though.
|
Agree, I also would repolishing the blade, it will look much better after this.